SIZE
RANGE : 0D 1.5MM TO 100MM WT: 0.2MM
MIN |
|
TRADE
NAME : SVMC Brass 70/30 |
|
| APPLICATION
: |
Sugar
Industry, Hand Pumps, Plumbing, Furniture,
General Engineering, Ammunitions. |
|
|
| |
CHARACTERISTIC
|
| |
| A
Copper and Zinc Alloy Containing amount of Arsenic.
This is added as an inhabitor Arsenic Against dezincification.
This Alloy exhibits the good combination of strength
and ductility. and is commonly selected whenever
exellent Cold working properties and most common
low cost are desirable. Severe environment must
be consider to predict corrosion behavior. the alloy
be often used for variety of deep drawn components. |
| |
|
TEST:
|
| ww |
| |
Drift
test, Flattening test, Mercurous nitrate test,
Hydraulic test as per specification. |
|
| |
| CHEMICAL
COMPOSITION OF BRASS |
| |
ALLOY
|
STD
APPLIED
|
ALLOY
DENOTATION
|
SYMBOL
|
CU
|
PB
|
FE
|
ZN
|
P
|
AL
|
SN
|
AS
|
TOTAL
IMPURITIES |
Svmc
Brass
63/37
|
BS
|
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
| ASTM |
B-135
|
C-27200
|
62.0-65.0
|
0.07
|
0.07
|
REMAIN
|
- |
- |
- |
- |
|
| DIN |
17671
|
CuZn
37
|
62.0-64.0
|
0.1
|
0.1
|
REMAIN |
- |
- |
0.1
|
- |
0.1 |
| NFA |
-
|
-
|
- |
- |
- |
- |
- |
- |
- |
- |
- |
| JIS |
H
3300
|
C
2700
|
63.0-67.0
|
0.07 |
0.05
|
REMAIN |
- |
- |
- |
- |
|
| IS |
407
|
CuZn
37
|
62.0-65.0
|
0.3
|
0.1
|
REMAIN |
- |
- |
- |
0.06
|
0.06 |
| |
|
|
|
|
|
|
|
|
|
|
|
|
Svmc
Brass
70/30 |
BS |
2871
PART3 |
CZ
- 126 |
69.0-71.0 |
0.07
|
0.06
|
REMAIN |
- |
- |
- |
0.02-0.06
|
0.3
|
| ASTM |
B-135
|
C
26000
|
68.5-71.5
|
0.07
|
0.05
|
REMAIN |
- |
- |
- |
- |
- |
| DIN |
17671
|
CuZn
30-2.0265
|
69.0-71.0
|
0.05
|
0.05
|
REMAIN |
- |
- |
0.05
|
- |
0.1 |
| NFA |
51-102
|
CuZn30
|
68.5-71.5
|
0.07
|
0.06
|
REMAIN |
- |
- |
- |
- |
0.3 |
| JIS |
H-
3300
|
C2600
|
68.5-71.5
|
0.07 |
0.05
|
REMAIN |
- |
- |
- |
- |
- |
| IS |
1545
|
CuZn
30 AS
|
69.0-71.0
|
0.07 |
0.06
|
REMAIN |
- |
- |
- |
0.02-0.06 |
0.3 |
|
| |
| PHYSICAL
COMPOSITION OF BRASS |
| |
| ALLOY |
STD
APPLIED
|
SYMBOL |
CONDITION |
YIELD,
STRENGTH N/mm2
|
TENSILE
N/mm2
|
ELONGATION
%
|
HARDNESS
HV 5
|
GRAIN
SIZE
Mm (75X) |
Svmc
Brass 63/37
|
BS
|
|
|
|
|
|
|
- |
ASTM
|
C
27200
|
H
58, H 80
|
- |
370
MIN., 455 MIN.
|
-
|
- |
- |
DIN
|
CuZn
37 |
F
29, F 37
|
180
MAX, 200 MIN.
|
290-370,
370-440
|
50
MIN, 27MIN
|
- |
- |
NFA
|
-
|
-
|
- |
-
|
-
|
- |
- |
JIS
|
C
2700 |
0,
1/2H, H
|
- |
294MIN,
373MIN , 451MIN.
|
40MIN,
20MIN
|
- |
.025-.06 |
| IS |
CuZn
37
|
O,
TA, HD
|
- |
285MIN,
320MIN, 400MIN.
|
- |
80MAX,
80-110, 130MIN.
|
- |
| |
|
|
|
|
|
|
|
|
Svmc
Brass 70/30
|
BS
|
CZ
- 126
|
M,
TA, O
|
- |
- |
- |
150MIN,
80-105 , 75 MAX.
|
0.05
MAX |
ASTM
|
C
2600
|
H
58, H 80 |
- |
370MIN,
455MIN.
|
- |
- |
- |
DIN
|
CuZn
30-2.0265
|
F28,
F35, F42.
|
180MAX,200MAX,
320MAX.
|
280-350,350-420,
420MIN.
|
- |
- |
- |
| NFA |
- |
- |
- |
- |
- |
80-105 |
0.010-0.45 |
JIS
|
C2600 |
O,
0H, 1/2H, H
|
- |
275MIN,275MIN,
373MIN,451MIN.
|
45MIN,
45MIN ,20MIN. |
- |
025-.060,035MIN |
IS
|
CuZn
30 AS |
O,
TA, HD
|
- |
375MAX,340MIN,
385MIN |
55
MIN |
80MAX,
80-105 , 130MIN.
|
- |
|
| |
| ADMIRALTY
BRASS TUBES
| ALUMINIUM
BRASS | 63/37
& 70/30 BRASS TUBES | WEIGHT
OF BRASS IN VARIOUS SIZES & GAUGES - EXTERNAL
DIAMETER | WEIGHT
OF BRASS RODS/BARS IN KILOGRAMS PER METER |
| |
|
|