SIZE RANGE : OD 4MMTO 100MM 0.2MM MIN.
TRADE NAME : SVMC Albrass
APPLICATION : Power Plants, Desalination Plants, Heat Exchanged adaptors, Refineries, Offshore Oil Rigs, Condensers, Ferrules, Evaporator, and Distillers
 
CHARACTERISTIC
 
A Copper Zinc Alloy containing tin and small amount of Arsenic which is, added as an inhibitor against dezincification. Inhibited Aluminum Brass resists the action of high velocity salt and brackish water and is commonly used for condenser tube. The outstanding characteristics of Aluminum Brass are the high resistance to impingement Attack Tubes of this alloy are recommended For use in marine and land power stations where cooling water velocities are high and where inhibited admiralty brass has failed Impingement
 
Guide to the selection of tube material:
ww
  Sea Water: -
a. Dissolved salts more than 2000 ppm
b. Suspended solids more than 30 ppm
c. H2C or Ammonia is less than 1 ppm
d. Permissible average velocity of water 2.0-2.5 miters/sec.
 
TEST:
ww
  Drift test, Flattening test, Mercurous nitrate test, M.N test, Eddy current test as per specification.
 
CHEMICAL COMPOSITION OF BRASS
 
ALLOY
STD APPLIED
ALLOY DENOTATION
SYMBOL
CU
PB
FE
ZN
P
AL
SN
AS
TOTAL
IMPURITIES
Svmc Aluminium
Brass
   BS   2871 PART3  CZ - 110
 76.0-78.0
 0.07
  0.06 REMAIN  -  1.8-2.3
 -  0.02-0.06
  0.3
   ASTM   B - 111  C 68700
 76.0-79.0
 0.07
  0.06 REMAIN  -  1.8-2.5
 -  0.02-0.06
 -
  DIN   1785  CuZn20 AL2
 76.0-79.0
 0.07
 0.07 REMAIN   0.01  1.8-2.3
 -  0.02-0.035
  0.1
   NFA   51-102  CuZn 22 AL2
 76.0-79.0
 0.07
  0.06 REMAIN  -  1.8-2.5
 -  0.02-0.06
   0.3
   JIS   H- 3300  C 6870
 76.0-79.0
 0.07
  0.06 REMAIN  -  1.8-2.5
 -  0.02-0.06
 -
  JB   1545  CuZn 21 AL2 AS
 76.0-78.0
 0.07
  0.06 REMAIN  -  1.8-2.3
 -  0.02-0.06
   0.3
 
PHYSICAL COMPOSITION OF BRASS
 
ALLOY STD APPLIED

SYMBOL CONDITION YIELD, STRENGTH N/mm2
TENSILE N/mm2
ELONGATION %
HARDNESS
HV 5
GRAIN SIZE
Mm (75X)
Svmc Aluminium Brass  BS
 CZ - 110
 M, TA, O
 -  -  - 150MIN, 80-110,  , 75 MAX
 0.05 MAX.
 ASTM
 C 68700
0 61
 125-105  345
 -  -  .010-.045
 DIN
 CuZn20 AL2
 F 39, F 34
 150-230, 120-180  390 MIN, 340MIN.
 45MIN, 55MIN.
 -  -
 NFA
 CuZn 22 AL2
 -  -  -  -  80-130
  .010-.045
 JIS
 C 6870
 O
 -  373
 40
 -   .010-.045
 IS  CuZn 21 AL2AS
 O, TA, oD
 400mpaMax,335mpa  Max,415mpaMax
 -  85 Max, 80-  110,130Min
 -   .010-.045
 